Galil (Gold)
|
| Smith-Emery
Test Results |
|
|
| Technical
Information |
ASTM
Test Method |
Value |
|
Law
Engineering & Environmental Services Tests |
| Absorption
By Weight% |
C97 |
1.17 |
|
Technical
Information |
ASTM
Test Method |
Value |
| Density,
lbs./cu. ft |
C97 |
158 |
|
Absorption
By Weight% |
C
373-88 |
0.74 |
| Static
Coefficient of Friction-Wet |
C1028-89 |
0.81 |
|
Static
Coefficient of Friction-Wet |
C1028-89 |
0.58 |
| Static
Coefficient of Friction-Dry |
C1028-89 |
0.79 |
|
Static
Coefficient of Friction-Dry |
C1028-89 |
0.79 |
| Flexural
Strength, psi |
C880-M |
1,529 |
|
Wear
Index |
C501-84 |
16.1 |
|
|
|
Breaking
Strength |
C648-84 |
647.0 |
|
MOH's
Hardness |
MOH's
Hardness Procedure |
4.0 |
|
Wear
Index |
C501-84 |
11.9 |
Hebron White |
| Smith-Emery
Test Results |
|
Law
Engineering & Environmental Services Tests |
| Technical
Information |
ASTM
Test Method |
Value |
|
Technical
Information |
ASTM
Test Method |
Value |
| Absorption
By Weight% |
C97 |
0.78 |
|
Absorption
By Weight% |
C
373-88 |
1.62 |
| Density,
lbs./cu. ft |
C97 |
164 |
|
Static
Coefficient of Friction-Wet |
C1028-89 |
0.55 |
| Static
Coefficient of Friction-Wet |
C1028-89 |
0.81 |
|
Static
Coefficient of Friction-Dry |
C1028-89 |
0.75 |
| Static
Coefficient of Friction-Dry |
C1028-89 |
0.79 |
|
Wear
Index |
C501-84 |
11.9 |
| Flexural
Strength, psi |
C880-M |
1,157 |
|
Breaking
Strength |
C648-84 |
645.0 |
| Compressive
Strength, psi |
C170 |
11,289 |
|
MOH's
Hardness |
MOH's
Hardness Procedure |
4.0 |
| Abrasion
Resistance, Hardness |
C241 |
10.5 |
|
|
Hebron Pink |
| Smith-Emery
Test Results |
|
Law
Engineering & Environmental Services Tests |
| Technical
Information |
ASTM
Test Method |
Value |
|
Technical
Information |
ASTM
Test Method |
Value |
| Absorption
By Weight% |
C97 |
0.72 |
|
Absorption
By Weight% |
C
373-88 |
0.72 |
| Density,
lbs./cu. ft |
C97 |
164 |
|
Static
Coefficient of Friction-Wet |
C1028-89 |
0.59 |
| Static
Coefficient of Friction-Wet |
C1028-89 |
0.81 |
|
Static
Coefficient of Friction-Dry |
C1028-89 |
0.82 |
| Static
Coefficient of Friction-Dry |
C1028-89 |
0.79 |
|
Wear
Index |
C501-84 |
13.7 |
| Flexural
Strength, psi |
C880-M |
1,529 |
|
Breaking
Strength |
C648-84 |
645.0 |
| Compressive
Strength, psi |
C170 |
11,380 |
|
MOH's
Hardness |
MOH's
Hardness Procedure |
4.0 |
| Abrasion
Resistance, Hardness |
C241 |
10.5 |
|
|
Ramon Gray |
| Smith-Emery
Test Results |
|
|
|
| Technical
Information |
ASTM
Test Method |
Value |
|
| Absorption
By Weight% |
C97 |
0.86 |
|
| Density,
lbs./cu. ft |
C97 |
163 |
|
| Static
Coefficient of Friction-Wet |
C1028-89 |
0.78 |
|
| Static
Coefficient of Friction-Dry |
C1028-89 |
0.74 |
|
| Flexural
Strength, psi |
C880-M |
1,254 |
|
|
Ramon Gold
|
|
Smith-Emery
Test Results
|
|
|
| Technical
Information |
ASTM
Test Method |
Value |
|
| Absorption
By Weight% |
C97 |
0.78 |
|
| Density,
lbs./cu. ft |
C97 |
169 |
|
| Flexural
Strength, psi |
C880-M |
1,248 |
|
| Compressive
Strength, psi |
C170 |
11,490 |
|
| Abrasion
Resistance, Hardness |
C241 |
10.5 |
|